- Paints And Varnishes Based, Incl. Enamels And Lacquers, On Synthetic Polymers Or Chemically Modified Natural Polymers, Dispersed Or Dissolved In A Non-aqueous Medium, And Solutions Of Products Of Headings 3901 To 3913 In Volatile Organic Solvents, Containing > 50% Solvent By Weight (excl. Those Based On Polyesters And Acrylic Or Vinyl Polymers And Solutions Of Collodion)
Double anticorrosion epoxy powder coating (Externa
Product Images
Product Property
Product Status : | New |
Sample Available : | yes |
Shipment Terms : | fob,cfr,cif,Negotiable |
Payment Mode : |
T/T,L/C,cash,cheque,WesternUnion,MoneyGram,Negotiable |
Description
Introduction: This double epoxy powder adopts many kinds of function of epoxy resin, curing agent, both bottom coating and other anti-corrosion epoxy powder coating have excellent anticorrosion performance, external coating stand out protective properties on the basis of corrosion, can be widely used in more stringent corrosion environment, especially especially traversing pipeline for mountains, rivers and hills region.
Feature:
1. Very good adhesion with the substrate and epoxy.
2. Strong permeability and corrosion resistance
3. The coating has excellent high temperature cathodic disbonding resistance.
4. High surface hardness, strong coating density, good ability to resist plant roots puncture
Power specification
Test Items | Technical Indicators | Test Method | |
Appearance | Even color, no caking | visual | |
Particle size distribution % | 150μm Sieve the powder | ≤4 | Q/CNPC 38-2002 appendix C |
250μm Sieve the powder | ≤0.2 | Q/CNPC 38-2002 appendix C | |
volatile matter content (%) | ≤ 0.6 | Q/CNPC 38-2002 appendix B | |
Gel time (205±3)℃(s) | ≥12 | Q/CNPC 38-2002 appendix A | |
Curing time (230℃)min | ≤ 3 | SY/T 0315-2005 | |
magnetic material content(%) | ≤ 0.002 | GB/T 6570 |
Coating Specification
Test Items | Technical Indicators | Test Method |
Appearance | smooth,uniform color, no bubble , no cracking and sinkhole, allow light crack | visual |
24h or 48h adhesion | 1~2 | SY/T 0315-2005 |
24h or 48h cathodic disbonding resistance(mm) | ≤6 | SY/T 0315-2005 |
cathodic disbonding resistance 28d(mm) | ≤ 8 | SY/T 0315-2005 |
Porosity of bottom section | 1~4 | SY/T 0315-2005 |
Porosity of underlying surface | 1~4 | SY/T 0315-2005 |
2° bending resistant(0°or -30°) common level | No cracking | Q/CNPC38-2002 appendix D |
1.5°bending resistant(0°or-30°)Intensify Level | No cracking | Q/CNPC38-2002 appendixD |
10J Impact(common level) | No pinehole | Q/CNPC 38-2002 appendix E |
15J Impact Intensify Level | No pinehole | Q/CNPC 38-2002 appendix E |
scratch resistant, 30Kg, common level | Scratch depth≤350μm No leaking point | Q/CNPC 38-2002 appendix F |
scratch resistant,50Kg, Intensify Level | Scratch depth≤500μm No leaking point | Q/CNPC 38-2002 appendix F |
Carried Standard: Q/CNPC 38-2002
Application Area: Corrosion environment is complex, especially traversing pipeline for mountains, rivers and hills region.
Applicable process: Electrostatic Coating
Notes:
1. Steel surface should be no oil and water, surface quality should reach Sa2 1/2 level (GB/T8923), anchor pattern depth 50-90mm, clean dust and abrasive attached to the steel surface
2. Product should be stored in ventilated, dry, indoor temperature below 30 ℃, away from heat, corrosive chemicals and chemical solvents, avoid bright light, the maximum stack height should not exceed 4 layers, avoid prolonged pressure, ensure airtight box. In case the clot and damp affects the fluidization performance.