Product performance

PZX-L is a new resin developed specifically to meet the technical requirements for hot melt road marking paint, PZX-L is very suitable to be used in hot melt road marking paint.It can enhance the paint’s toughness, hardness and adhesive, and form a smooth surface, and by adding additive to make resin at the Four Seasons always in a stable condition, and have good compatibility with rosin resins. In the high-end mixed paint, it can make paint film form a water-resistant, UV resistant, chemical-resistant properties, and remarkably improves appearance and aridity.

PRODUCT SPECIFICATIONS

Specification	Test Method	Unit	Specification Range
Softening Point	ASTM-E-28	℃	95-105
Color	ASTM-D1544	GC	5 Max
Melt Viscosity	ASTM-D-3236	MPa·s	220 Max
Insoluble	ASTM-E-99	Vol%	0.1 Max
Acid Value	ASTM-D-974	Mg KOH/g	1 Max

Application field recommended: Hot Melt Road Marking Paint

Other use: Pressure Sensitive Adhesive

The road marking paint made by PZX-L hydrocarbon resin has the following characteristics:

Ø Light color

Ø Good fluidity

Ø High anti-fraction

Ø Even distribution of filling material without sedimentation.

Ø Good heat stability

Ø Fast drying speed

Ø Good weather resistance, adhesive force and stain resistance.

Detailed product description of the road marking paint made by PZX-L hydrocarbon resin:

Ø Chemical composition:PZX-L hydrocarbon resin, EVA, PE wax, fillers materials and so on

Ø Standard:

1. Color :standard color is yellow and white.Optional color is red, blue, green and black

2. Density:2.01g/cm3

3. Compression strength:21.9MPa

4. Softening point:109℃

5. Wet film thickness:1800-2000μm

6. Dry film thickness:1800-2000μm

7. Glass beads content:5%

8. Dosage:theory of 0.25 square meters/kg

9. The surface drying time:3 min;Full dry:10 min

10. Times:suggest 1 time

11. Shelf life:two years, over the period, if it can be used continually, as appropriate.