Drill Stabilizer for Raise Boring Machine
Product Images
Product Property
Product Status : | New |
Sample Available : | no |
Shipment Terms : | fob,cfr,cif |
Payment Mode : |
T/T,L/C,WesternUnion |
Description
We could manufacture all kinds of drill stabilizer used for raise boring machine,
The nominal diameter size is from 9" to 17-1/2", the length is from 48" to 60".
The drill stabilizer could be divided into straight ribs stabilizer ( Tungsten carbide hardfacing )
Straight ribs ( Weld-on hardfacing ) spiral ribs ( Tungsten carbide )
The detail information refer to the below data sheet.
We choose SAE4330V MOD material, Material specification:
General description:
Material: NCMV33/03 (SAE 4330 V-MOD)
Chemical:
C: 0.28 Min. /0.37 Max.
Mn: 0.45Min. /0.65Max.
P: <= 0.015
S: <= 0.015
Si: 0.1 Min. /0.3 Max.
Ni: 2 Min. /3 Max.
Cr: 0.8 Min. /1.1 Max.
Mo: 0.4 Min. /0.65 Max.
V: 0.05 Min. /0.15 Max.
Mechanical:
UTS: 1033 MPa Min. (T), 1033 MPa Min. (L).
Yield at 2% offset: 964 MPa Min. (T), 964 MPa Min. (L).
Elongation in 2": 10.7% Min. (T), 15% Min. (L).
Reduction of area: 32% Min. (T), 45% Min. (L).
% Shear: 70%.
BHN @ 1" below surface: 321-364 BHN.
CVN @ +70ºF with radial notch: 90J (L) Min., 50J (T) Min.
Cleanliness: As per ASTM E45-97 method A, A/B: Thin≤ 2.0; Heavy≤ 1.5; C/D: Thin≤ 1.0; Heavy≤ 1.0.
Austenite grain: As per ASTM E112-96, fine grade of 5 or finer.
The nominal diameter size is from 9" to 17-1/2", the length is from 48" to 60".
The drill stabilizer could be divided into straight ribs stabilizer ( Tungsten carbide hardfacing )
Straight ribs ( Weld-on hardfacing ) spiral ribs ( Tungsten carbide )
The detail information refer to the below data sheet.
We choose SAE4330V MOD material, Material specification:
General description:
Material: NCMV33/03 (SAE 4330 V-MOD)
Chemical:
C: 0.28 Min. /0.37 Max.
Mn: 0.45Min. /0.65Max.
P: <= 0.015
S: <= 0.015
Si: 0.1 Min. /0.3 Max.
Ni: 2 Min. /3 Max.
Cr: 0.8 Min. /1.1 Max.
Mo: 0.4 Min. /0.65 Max.
V: 0.05 Min. /0.15 Max.
Mechanical:
UTS: 1033 MPa Min. (T), 1033 MPa Min. (L).
Yield at 2% offset: 964 MPa Min. (T), 964 MPa Min. (L).
Elongation in 2": 10.7% Min. (T), 15% Min. (L).
Reduction of area: 32% Min. (T), 45% Min. (L).
% Shear: 70%.
BHN @ 1" below surface: 321-364 BHN.
CVN @ +70ºF with radial notch: 90J (L) Min., 50J (T) Min.
Cleanliness: As per ASTM E45-97 method A, A/B: Thin≤ 2.0; Heavy≤ 1.5; C/D: Thin≤ 1.0; Heavy≤ 1.0.
Austenite grain: As per ASTM E112-96, fine grade of 5 or finer.